Refractories Slide Gate Plate

Vrste i principi rada kliznih ploča: Uređaj klizne mlaznice se sastoji od gornje i donje klizne ploče od vatrostalnih materijala i mehaničke pogonske konstrukcije, a postavlja se izvan dna lonca. Gornja klizna ploča je fiksna, a donja klizna ploča je pokretna. Prema načinu djelovanja vatrostalnih kliznih ploča, mogu se podijeliti u tri kategorije: 1) Linearni klipni tip: 2) Linearni pogonski tip: 3) Rotacioni tip. Pokretanjem vučne šipke, vatrostalna ploča klizne kapije klizi naprijed-nazad u pravoj liniji. Kada su rupe za livenje na gornjoj i donjoj vatrostalnoj cigli kliznih vrata raspoređene, gornji otvor mlaznice se napuni drenažnim peskom, a čelični lonac se može napuniti čelikom; kada se rupe za livenje preklapaju, drenažni pesak automatski teče, a zatim se izliva, a brzina izlivanja se može kontrolisati stepenom preklapanja rupa za livenje.

Klizna ploča je ključna komponenta koja određuje funkciju klizne mlaznice i igra ulogu u kontroli i regulaciji protoka rastaljenog čelika. Zbog stalnog kontakta klizne ploče sa -rastopljenim čelikom na visokim temperaturama (posebno dio rupe za livenje), korozija je ozbiljna i uslovi upotrebe su teški. Vatrostalna klizna ploča mora imati dobra svojstva kao što su visoka čvrstoća, otpornost na koroziju i otpornost na ljuštenje. Tokom procesa izlivanja, osigurava se da rastopljeni čelik ne može procuriti između vatrostalnih ploča kliznih vrata. Vatrostalna ploča kliznog zatvarača mora imati sljedeća svojstva

(1) Ravnost klizne površine<0.05mm

(2) Visoka mehanička čvrstoća

(3) Jaka otpornost na eroziju rastopljenim čelikom i rastopljenom troskom;

(4) Odlična antioksidativna svojstva

(5) Dobra stabilnost termičkog udara.

Zaštita od brtvljenja klizne mlaznice lonca uglavnom je na spoju između gornje mlaznice i gornje klizne ploče i donje klizne ploče i donje mlaznice. Tokom procesa izlivanja, obično nakon izlivanja jedne ili dvije peći od rastopljenog čelika, donja klizna ploča i odvodni otvor moraju se zamijeniti i ponovo sastaviti. Zaštita za zaptivanje koristi zaptivne jastučiće od vlakana ili gline kako bi se osigurala visoka čistoća rastopljenog čelika i ujednačenost unutrašnjeg kvaliteta livene ploče.

zapaliti u vatrostalnu ploču klizne kapije

U pečenoj aluminijumskoj ugljičnoj kliznoj ploči, ne samo da se organsko vezivo karbonizira i koksuje tokom pečenja, formirajući ugljičnu vezu u cigli, već se i aditivi, kao što je metalni silicijum, mogu kombinovati sa ugljikom da formiraju Sic kada se redukuju i peče.<1300°C. , and a ceramic bond is formed within the brick body. Therefore, there is a dual bonding system of ceramic bonding and carbon bonding in the fired aluminum carbon sliding plate. It significantly improves the strength of the refractories slide gate plate, and even after the carbon is burned out during use, it can maintain sufficient residual strength because it is a ceramic bonding system. After the refractories slide gate plate is burned, it is usually soaked in oil. Vertical or horizontal vacuum-pressurized oil immersion devices are generally used in oil immersion. After the slide is preheated, put it into the oil immersion tank, and evacuate it to a vacuum℃of 650mmHg or above, introduce heated tar or asphalt, and pressurize the oil to 8~16kgf/cm2 or higher to make the tar or asphalt Being sucked into the open air holes of the refractories slide gate plate. The cast holes in the refractories slide gate plate can be made during molding, or they can be formed into a whole plate without holes and then drilled later. Most people think that drilling is beneficial to improve the quality of the refractories slide gate plate. In addition, wrapping and hooping the refractories slide gate plate with thin iron sheets is considered an important measure to ensure the safe use of the refractories slide gate plate. It can prevent the refractories slide gate plate from breaking during use, and because this metal hoop is wrapped very tightly, it has limitations. The propagation of cracks in materials, especially the effect of crack opening.

Vatrostalna klizna ploča visokih performansi

To je ne-aluminijska karbonska vatrostalna klizna ploča s relativno jednostavnim procesom, niskom cijenom i dobrim učinkom upotrebe. Sastojci ove vrste vatrostalnih kliznih ploča su slični onima za pečene vatrostalne klizne ploče. Koristi sirovine kao što su korund, mulit, korund, grafit u listićima, silicijum karbid i silicijum prah, a kao vezivo dodaje fenolnu smolu. Nakon miješanja, oblikovanja, termičke obrade i mehaničke obrade to je gotov proizvod. U poređenju sa kliznim vratima od pečenog aluminijuma od ugljenika, nesagorele vatrostalne klizne ploče ne zahtevaju pečenje, potapanje u ulje i termičku obradu retorte tokom proizvodnje, što pojednostavljuje proces proizvodnje, ali je jačina manja, a poroznost je nešto veća. Praksa je dokazala da klizna ploča koja ne gori-ima dobar učinak kada se koristi na loncu srednjih-konvertera i električnih peći, a neke čak i nadmašuju klizna ploča-uronjena na ulje.

Kako instalirati i koristiti vatrostalne ploče za klizne kapije

Količina i tvrdoća vatrostalne gline između klizne ploče i mlaznice treba da bude odgovarajuća kako bi spoj bio ujednačen i odgovarajuće čvrstoće kako bi se povećala -stopa samootvaranja mlaznice, izbjeglo sagorijevanje i drenaža kisika, smanjila oksidacija klizne ploče i proširenje rupe kako bi se spriječilo da se mlaznica "okreće" kada se izlije rastopljeni čelik. Pojavu pojave "šljake" treba smanjiti kako bi se smanjila erozija šljake na površini klizne ploče. Prilikom kontrole protoka čelika za kontinuirano lijevanje i zatvaranja operacije nakon izlijevanja, hod 1 treba sačuvati upuhujući kisik kako bi se uklonio zaostali čelik i spriječio nepravilan rad zaostalog čelika i izazivanje prekomjernog širenja klizne ploče.